Technical data


1.General Chemical Resistance
Where exposure to a chemical will be prolonged or at elevated temperatures, tests should be performed
to prove the suitability of the product for that specific use.


Product Dilute Acids (less than 30%) Concentrated Acids (30% or more) Weak Alkalis Strong Alkalis Chlorinated Solvents Aldehydes Ketones Esters
Glasbord® -P panel
G to E
G to E
G
E
G to E

Key:
E = excellent, outstanding
G = good, probably acceptable
F = fair, test before using
P = poor, not recommended
NONWARRANTY
- We believe all information given is accurate. It is offered in good faith, but without guarantee. Since conditions of use are beyond our control, all risks are assumed by the user.

2.Stain Resistance To Food And Miscellaneous Products
Stain resistance of Glasbord-P with Surfaseal, Fire-X Glasbord with Surfaseal, Kemlite L-1062, and Glasbord-REI is very similar:

Stain
ASTM D22991
122oF (50oC), 16 hrs.
ASTM D13082
77o-86oF (25o-30oC), 24 hrs.
Blood (beef)
Superficial
Superficial
Brown Shoe Polish
Considerable
Considerable
Butter
Unaffected
Unaffected
Crayon (green)
Superficial
Superficial
Mustard
Unaffected
Superficial
Oil (crankcase)
Superficial
Superficial
Potato (white)
Unaffected
Unaffected
Red CabbageUnaffectedUnaffected
TeaUnaffectedUnaffected
Tomato AcidUnaffectedUnaffected


Key:
Unaffected = wipes off easily with damp cloth and mild soap; no color or surface change
Superficial = stain removed easily with water and/ or mild abrasive
Considerable = stain not completely removable
1) ASTM D2299 tests stain resistance of applied coating
2) ASTM D1308 tests stain resistance of a product's natural surface

3. Resistance To Specific Chemicals

Chemical
Panaels
General Comments
Acetic Acid, concentrated
E

Acetic Acid, 5%
E

Ammonium Hydroxide, concentrated
E

Ammonium Hydroxide, 10%
C
Caused both to turn yellow
Aniline
P1 Caused both to turn red
Bleach Solution
C
Caused panels to turn yellow
Citric Acid, 10%
E

Detergent Solution
C
Caused panels to turn yellow
Distilled Water
E

Ethyl Acetate
P1
Ethyl Alcohol, 95%
C
Caused panels to turn yellow
Ethyl Alcohol, 50%
G1
Formaldehyde
E

Heptane
F

Hydrochloric Acid, 10%
E

Hydrogen Peroxide, 3%
C
Caused panels to turn yellow
Isooctane
G1
Lactic Acid, 10%
E

Mineral Oil
E

Nitric Acid, 40%
E

Nitric Acid, 10%
E

Oleic Acid
E

Olive Oil
E

Potassium Iodide Solution, 10%
E

Soap Solution
E

Sodium Chloride Solution, 10%
P1 Caused panels to turn yellow
Sodium Chloride Solution, 60%
P

Sodium Hydroxide Solution, 10%
P
Caused panels to turn yellow
Sodium Hydroxide Solution, 1%
P
Caused panels to turn yellow
Sodium Hypochlorite Solution, 4-6%
E

Sulfuric Acid, 30%
G1
Sulfuric Acid, 3%
G1
Toluene
G1 Caused panels to turn yellow
Transformer Oil
G1
Turpentine
G1

Ratings Key:
E = (Excellent): Suitable for use in most exposure conditions.
G = (Good): Probably suitable for use; testing under specific exposure conditions is suggested.
F = (Fair): Possibly unsuitable for use; testing under specific exposure conditions is recommended.
P = (Poor): Unsuitable for use in most exposure conditions.
C = Color change
NT = Not tested

General Notes:

• Ratings are based on a combination of visual observations, and mechanical strength test results.
• All testing was done at 770 +- 100 F.Performance ratings are not necessarily valid outside of that temperature range.
• Test ratings are based on white material; non-white panels could show additional visual changes.
• Test was run per Crane Kemlite product development procedure #8125: surface chemical resistance.
   In this procedure the  chemicals are exposed to the surface of the panel for 7 days.


4.PHYSICAL PROPERTIES
Glasbord-P with Surfaseal is a durable, flexible, interior wall panel of fiberglass reinforced plastic (frp). The panel has a Class C rating for flame spread and smoke development. It will not mildew, rot, or corrode and exhibits excellent resistance to mild chemicals and moisture.

PROPERTY
TYPICAL VALUE
2.3 mm THICKNESS
TEST METHOD
Flexural Strength
59 MPa
ASTM D790
Flexural Modulus
2413 MPa
ASTM D790
Tensile Strength
34 MPa
ASTM D638
Tensile Modulus
4137 MPa
ASTM D638
Barcol Hardness
35
ASTM D2583
Izod Impact Strength
0.37 J/mm
ASTM D256
Gardner Impact Strength
1.81 J/mm
ASTM D3029
Coefficient of Linear Thermal Expansion
29 ľm/m 0C
ASTM D696
Water Absorption (%)
0.16%/24 hrs @250C
ASTM D570
Specific Gravity
1.8
ASTM D792
TR Value
0.018 hr m2 0C/kcal
ASTM D177
Surface burning characteristics
Class C
ASTM E84
Taber Abrasion Resistance
(cs-17 wheels, 500 g. wt., 25 cycles)
0.038% max wt loss
Taber Abrader